General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.72 g/cm³ Show Material materials with Densidad of 1.72 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 1.8 % Show Material materials with Elongación of 1.8 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 9.6 GPa Show Material materials with Módulo de flexión of 9.6 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 11 GPa Show Material materials with Módulo elástico of 11 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 170 MPa Show Material materials with Resistencia a la flexión of 170 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.8E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 1.80 MPa | 214 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 214 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 150 °C Show Material materials with Relative temperature index, mechanical impact of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 150 °C Show Material materials with Relative temperature index, mechanical strength of 150 °C | UL 746B | 120mil | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-1 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-1 class, Thickness tested: 3 mm, UL recognition: yes - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 40% Glass Fiber and Mineral Powder | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 120°C, Min. mold temperature: 100°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |