General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 9.5 % Show Material materials with Absorción de agua of 9.5 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.13 g/cm³ Show Material materials with Densidad of 1.13 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |||
Elongación | 23.0 °C | 50 % Show Material materials with Elongación of 50 % | ISO 527-1/-2 | 50mm/min | ||
Elongación transversal | 23.0 °C | 400 % Show Material materials with Elongación transversal of 400 % | ISO 527-3 | Film Properties | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Hardness, Ball Indentation | 23.0 °C | 170 MPa Show Material materials with Hardness, Ball Indentation of 170 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 80 MPa Show Material materials with Límite elástico of 80 MPa | ISO 527-1/-2 | ||
Límite elástico transversal | 23.0 °C | 31 MPa Show Material materials with Límite elástico transversal of 31 MPa | ISO 527-3 | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.9 GPa Show Material materials with Módulo elástico of 2.9 GPa | ISO 527-1/-2 | ||
Resistencia a la tracción | 23.0 °C | 90 MPa Show Material materials with Resistencia a la tracción of 90 MPa | ISO 527-3 | Film Properties | ||
Resistencia a la tracción transversal | 23.0 °C | 80 MPa Show Material materials with Resistencia a la tracción transversal of 80 MPa | ISO 527-3 | Film Properties | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA | ||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6,-40°C, ISO 179/1eA | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 1680 J/(kg·K) Show Material materials with Calor específico of 1680 J/(kg·K) | of solid | ||
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Conductividad térmica | 23.0 °C | 0.24 W/(m·K) Show Material materials with Conductividad térmica of 0.24 W/(m·K) | of solid | ||
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 55 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Glow Wire Flammability Index, 40mil: 800 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.5 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.5 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm | |