General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 5.7 % Show Material materials with Absorción de agua of 5.7 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.45 g/cm³ Show Material materials with Densidad of 1.45 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 8 % Show Material materials with Elongación of 8 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 5.8 GPa Show Material materials with Módulo elástico of 5.8 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 87 MPa Show Material materials with Resistencia a la tracción of 87 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5.5 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 115 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 115 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 95 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 95 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |
Temperatura de fusión | 256 °C Show Material materials with Temperatura de fusión of 256 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |