General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.8 % Show Material materials with Absorción de agua of 1.8 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.13 g/cm³ Show Material materials with Densidad of 1.13 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.36 [-] Show Material materials with Coeficiente de Poisson of 0.36 [-] | |
Elongación | 23.0 °C | 9 % Show Material materials with Elongación of 9 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 3.8 % Show Material materials with Elongation at yield of 3.8 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 92 MPa Show Material materials with Límite elástico of 92 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 3.1 GPa Show Material materials with Módulo de flexión of 3.1 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.6 GPa Show Material materials with Módulo elástico of 3.6 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 2.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2.5 kJ/m² | ISO 179/1eA |
23.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 110 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 110 kJ/m² | ISO 179/1eU |
23.0 °C | 70 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 2 kJ/m² | ISO 180/1A |
-30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 2 kJ/m² | ISO 180/1A | |
23.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 3.5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2700 J/(kg·K) Show Material materials with Calor específico of 2700 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 7.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.6E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9.2E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 175 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 65 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO 75-1/-2 | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | IEC 60216-1 | 5000 hours | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 200 °C Show Material materials with Temperatura de reblandecimiento Vicat of 200 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 60 °C Show Material materials with Temperatura de transición del vidrio of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 850 °C, Glow Wire Flammability Index, 120mil: 800 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: SE - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 100 Hz | 23.0 °C | 4.2 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.2 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 30 kV/mm Show Material materials with Rigidez dieléctrica of 30 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm |