Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.07 g/cm³ Show Material materials with Densidad of 1.07 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |||
Elongación | 23.0 °C | 22 % Show Material materials with Elongación of 22 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.4 % Show Material materials with Elongation at yield of 4.4 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 65 MPa Show Material materials with Límite elástico of 65 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.5 GPa Show Material materials with Módulo elástico of 2.5 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 80 MPa Show Material materials with Resistencia a la flexión of 80 MPa | ISO 178 | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA | ||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4 kJ/m² | ISO 180/1A | ||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23°C, ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |
Temperatura de fusión | 218 °C Show Material materials with Temperatura de fusión of 218 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.86 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 250°C, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C |