General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.61 g/cm³ Show Material materials with Densidad of 1.61 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 0.9 % Show Material materials with Elongación of 0.9 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 13 GPa Show Material materials with Módulo de flexión of 13 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 13.1 GPa Show Material materials with Módulo elástico of 13.1 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 143 MPa Show Material materials with Resistencia a la flexión of 143 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 85 MPa Show Material materials with Resistencia a la tracción of 85 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.1E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 155 °C Show Material materials with Relative temperature index, electrical of 155 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 170 °C Show Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 170 °C Show Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | 120mil | |||
Temperatura de fusión | 249 °C Show Material materials with Temperatura de fusión of 249 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 825 °C, Glow Wire Ignition Temperature, 60mil: 775 °C, Glow Wire Ignition Temperature, 120mil: 850 °C, Railway classification: R22 -, Railway classification rating: HL1 - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 34 kV/mm Show Material materials with Rigidez dieléctrica of 34 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 350 V Show Material materials with Índice de seguimiento comparativo of 350 V | IEC 60112 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 33% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 280°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C | |