General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.1 % Show Material materials with Absorción de agua of 1.1 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.41 g/cm³ Show Material materials with Densidad of 1.41 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Dureza Rockwell M | 23.0 °C | 110 [-] Show Material materials with Dureza Rockwell M of 110 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 285 MPa Show Material materials with Hardness, Ball Indentation of 285 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 10 GPa Show Material materials with Módulo de flexión of 10 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 11 GPa Show Material materials with Módulo elástico of 11 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 300 MPa Show Material materials with Resistencia a la flexión of 300 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 210 MPa Show Material materials with Resistencia a la tracción of 210 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 60 kJ/m² | ISO 180/1U |
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 60 kJ/m² | ISO 180/1U | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A |
23.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 14 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2300 J/(kg·K) Show Material materials with Calor específico of 2300 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.4E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.4E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 255 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 255 °C Show Material materials with Temperatura de reblandecimiento Vicat of 255 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.7 mm, UL recognition: yes -, Oxygen index: 21 %, Glow Wire Flammability Index, 80mil: 650 °C, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 41 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 450 V Show Material materials with Índice de seguimiento comparativo of 450 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |