General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.51 g/cm³ Show Material materials with Densidad of 1.51 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.5 % Show Material materials with Elongación of 2.5 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 9.5 GPa Show Material materials with Módulo de flexión of 9.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10 GPa Show Material materials with Módulo elástico of 10 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 95 MPa Show Material materials with Resistencia a la tracción of 95 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2 kJ/m² | ISO 179/1eA |
23.0 °C | 3 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 2.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 2.5 kJ/m² | ISO 180/1A |
23.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 3.5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 3.6E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.6E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 263 °C Show Material materials with Temperatura de fusión of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |