General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.57 g/cm³ Show Material materials with Densidad of 1.57 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.3 % Show Material materials with Elongación of 2.3 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 9.7 GPa Show Material materials with Módulo elástico of 9.7 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 80 MPa Show Material materials with Resistencia a la tracción of 80 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 24 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 24 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Temperatura de fusión | 252 °C Show Material materials with Temperatura de fusión of 252 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Glow Wire Flammability Index, 15mil: 750 °C, Glow Wire Flammability Index, 30mil: 750 °C, Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 60mil: 750 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 15mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 875 °C, Glow Wire Temperature, No Flame, 30mil: 750 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber and Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |