General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.62 % Show Material materials with Absorción de agua of 0.62 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.69 g/cm³ Show Material materials with Densidad of 1.69 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Dureza Rockwell M | 23.0 °C | 100 [-] Show Material materials with Dureza Rockwell M of 100 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 2 % Show Material materials with Elongación of 2 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 13.5 GPa Show Material materials with Módulo de flexión of 13.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 15.5 GPa Show Material materials with Módulo elástico of 15.5 GPa | ISO 527-1/-2 |
Resistencia a la compresión | 23.0 °C | 230 MPa Show Material materials with Resistencia a la compresión of 230 MPa | ISO 604 |
Resistencia a la tracción | 23.0 °C | 182 MPa Show Material materials with Resistencia a la tracción of 182 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 60 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 11 kJ/m² | ISO 180/1A |
Resistencia al cizallamiento | 23.0 °C | 50 MPa Show Material materials with Resistencia al cizallamiento of 50 MPa | ASTM D 732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.3E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.3E-5 1/K | ISO 11359-1/-2 | ||
Conductividad térmica | 23.0 °C | 0.32 W/(m·K) Show Material materials with Conductividad térmica of 0.32 W/(m·K) | of solid | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 1.80 MPa | 226 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 226 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 8.0 MPa | 180 °C Show Material materials with Heat deflection temperature, 8.0 MPa of 180 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Temperatura de fusión | 252 °C Show Material materials with Temperatura de fusión of 252 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 230 °C Show Material materials with Temperatura de reblandecimiento Vicat of 230 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 120mil: 825 °C, Glow Wire Temperature, No Flame, 40mil: 775 °C, Glow Wire Temperature, No Flame, 60mil: 775 °C, Glow Wire Temperature, No Flame, 80mil: 775 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 4.4 [-] Show Material materials with Constante dieléctrica, 1 MHz of 4.4 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.5 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.5 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 32 kV/mm Show Material materials with Rigidez dieléctrica of 32 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 2 V Show Material materials with Índice de seguimiento comparativo of 2 V | UL 746A |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 120°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |