General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.3 % Show Material materials with Absorción de agua of 1.3 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.11 g/cm³ Show Material materials with Densidad of 1.11 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 5.5 % Show Material materials with Elongation at yield of 5.5 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.27 GPa Show Material materials with Módulo de flexión of 2.27 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 2.4 GPa Show Material materials with Módulo elástico of 2.4 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A |
23.0 °C | 16 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 16 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 1.80 MPa | 65 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |