General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.2 % Show Material materials with Absorción de agua of 1.2 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.41 g/cm³ Show Material materials with Densidad of 1.41 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 18 % Show Material materials with Elongación of 18 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 4.5 GPa Show Material materials with Módulo de flexión of 4.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 4.9 GPa Show Material materials with Módulo elástico of 4.9 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 80 MPa Show Material materials with Resistencia a la tracción of 80 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA |
-6.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |
23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU |
23.0 °C | 210 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 210 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 90 kJ/m² | ISO 180/1U |
23.0 °C | 190 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 190 kJ/m² | ISO 180/1U | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A |
-30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A | |
23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 9 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.4E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.5E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 205 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 205 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 256 °C Show Material materials with Temperatura de fusión of 256 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Oxygen index: 25 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 24 kV/mm Show Material materials with Rigidez dieléctrica of 24 kV/mm | IEC 60243-1 | Short Time, 2mm |
Volume resistivity | 23.0 °C | 1.00E+13 Ω·cm Show Material materials with Volume resistivity of 1.00E+13 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 400 V Show Material materials with Índice de seguimiento comparativo of 400 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 36% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |