Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 5.4 % Show Material materials with Absorción de agua of 5.4 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.45 g/cm³ Show Material materials with Densidad of 1.45 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 10 % Show Material materials with Elongación of 10 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 5.9 GPa Show Material materials with Módulo de flexión of 5.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 6 GPa Show Material materials with Módulo elástico of 6 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 135 MPa Show Material materials with Resistencia a la flexión of 135 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 87 MPa Show Material materials with Resistencia a la tracción of 87 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA |
23.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5.5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 95 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 95 kJ/m² | ISO 179/1eU |
23.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 130 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1940 J/(kg·K) Show Material materials with Calor específico of 1940 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 6.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.5E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 196 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 196 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 30mil | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 210 °C Show Material materials with Temperatura de reblandecimiento Vicat of 210 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.85 mm, UL recognition: yes -, FMVSS Class: SE - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |