General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Dureza Rockwell M | 23.0 °C | 103 [-] Show Material materials with Dureza Rockwell M of 103 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 3.8 % Show Material materials with Elongación of 3.8 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 200 MPa Show Material materials with Hardness, Ball Indentation of 200 MPa | ISO 2039-1 |
Módulo de flexión | 23.0 °C | 4.4 GPa Show Material materials with Módulo de flexión of 4.4 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5 GPa Show Material materials with Módulo elástico of 5 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
-6.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU |
23.0 °C | 73 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 73 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A |
-30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A | |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 13 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 258 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 105 °C Show Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | 120mil | |||
Temperatura de fusión | 263 °C Show Material materials with Temperatura de fusión of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 215 °C Show Material materials with Temperatura de reblandecimiento Vicat of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 21 %, Glow Wire Flammability Index, 15mil: 700 °C, Glow Wire Flammability Index, 30mil: 700 °C, Glow Wire Flammability Index, 40mil: 700 °C, Glow Wire Flammability Index, 60mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 44 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 14% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |