General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.02 g/cm³ Show Material materials with Densidad of 1.02 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.45 [-] Show Material materials with Coeficiente de Poisson of 0.45 [-] | |||
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | min. | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 0.9 GPa Show Material materials with Módulo de flexión of 0.9 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.9 GPa Show Material materials with Módulo elástico of 0.9 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 65 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 65 kJ/m² | ISO 179/1eA | ||
23.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 130 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23°C, ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2700 J/(kg·K) Show Material materials with Calor específico of 2700 J/(kg·K) | of melt | ||
Heat deflection temperature, 0.45 MPa | 55 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 55 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 48 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 48 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 221 °C Show Material materials with Temperatura de fusión of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | 55 °C Show Material materials with Temperatura de transición del vidrio of 55 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 27 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 260°C, Min. melt temperature: 250°C, Max. melt temperature: 280°C, Min. mold temperature: 40°C, Max. mold temperature: 80°C |