General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.8 % Show Material materials with Absorción de agua of 1.8 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.36 [-] Show Material materials with Coeficiente de Poisson of 0.36 [-] | |
Elongación | 23.0 °C | 10 % Show Material materials with Elongación of 10 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 3.8 GPa Show Material materials with Módulo elástico of 3.8 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 80 MPa Show Material materials with Resistencia a la tracción of 80 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 3 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 4.4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.4 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2590 J/(kg·K) Show Material materials with Calor específico of 2590 J/(kg·K) | of melt | ||
Heat deflection temperature, 0.45 MPa | 230 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 230 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 95 °C Show Material materials with Relative temperature index, mechanical impact of 95 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 110 °C Show Material materials with Relative temperature index, mechanical strength of 110 °C | UL 746B | 120mil | |||
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.82 mm, UL recognition: yes -, Oxygen index: 39 %, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 960 °C, Glow Wire Ignition Temperature, 15mil: 960 °C, Glow Wire Ignition Temperature, 60mil: 960 °C, Glow Wire Ignition Temperature, 120mil: 960 °C, FMVSS Class: DNI - |
Eléctrico
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |