General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 3.4 % Show Material materials with Absorción de agua of 3.4 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.53 g/cm³ Show Material materials with Densidad of 1.53 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.4 % Show Material materials with Elongación of 2.4 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 9 GPa Show Material materials with Módulo elástico of 9 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 130 MPa Show Material materials with Resistencia a la tracción of 130 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9.5 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 1910 J/(kg·K) Show Material materials with Calor específico of 1910 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 2.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.6E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.3E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.3E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 1.80 MPa | 243 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 243 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 235 °C Show Material materials with Temperatura de reblandecimiento Vicat of 235 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.83 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, FMVSS Class: DNI -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 25% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C | |