General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 3.6 % Show Material materials with Absorción de agua of 3.6 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.57 g/cm³ Show Material materials with Densidad of 1.57 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Dureza Rockwell M | 23.0 °C | 109 [-] Show Material materials with Dureza Rockwell M of 109 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 2.4 % Show Material materials with Elongación of 2.4 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 13 GPa Show Material materials with Módulo de flexión of 13 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 15 GPa Show Material materials with Módulo elástico of 15 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 330 MPa Show Material materials with Resistencia a la flexión of 330 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 240 MPa Show Material materials with Resistencia a la tracción of 240 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA |
-6.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 85 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 85 kJ/m² | ISO 179/1eU |
23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 87 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 87 kJ/m² | ISO 180/1U |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 13 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 12 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1610 J/(kg·K) Show Material materials with Calor específico of 1610 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.3E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 286 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 286 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 265 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 265 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 150 °C Show Material materials with Relative temperature index, mechanical impact of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 150 °C Show Material materials with Relative temperature index, mechanical strength of 150 °C | UL 746B | 120mil | |||
Temperatura de fusión | 300 °C Show Material materials with Temperatura de fusión of 300 °C | ISO 11357-1/-3 | first heat | |||
Temperatura de transición del vidrio | 135 °C Show Material materials with Temperatura de transición del vidrio of 135 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.85 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 29 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.2 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.2 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 35 kV/mm Show Material materials with Rigidez dieléctrica of 35 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C |