General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.45 g/cm³ Show Material materials with Densidad of 1.45 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.2 % Show Material materials with Elongación of 2.2 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 10.5 GPa Show Material materials with Módulo de flexión of 10.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10.8 GPa Show Material materials with Módulo elástico of 10.8 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 215 MPa Show Material materials with Resistencia a la flexión of 215 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 148 MPa Show Material materials with Resistencia a la tracción of 148 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 46 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 46 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.7E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 283 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 283 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Temperatura de fusión | 310 °C Show Material materials with Temperatura de fusión of 310 °C | ISO 11357-1/-3 | first heat | |||
Inflamabilidad | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes - |
Eléctrico
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 320°C, Max. melt temperature: 325°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |