General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 6.5 % Show Material materials with Absorción de agua of 6.5 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.21 g/cm³ Show Material materials with Densidad of 1.21 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Dureza Rockwell M | 23.0 °C | 90 [-] Show Material materials with Dureza Rockwell M of 90 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 4 % Show Material materials with Elongación of 4 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 180 MPa Show Material materials with Hardness, Ball Indentation of 180 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 4.7 GPa Show Material materials with Módulo de flexión of 4.7 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5 GPa Show Material materials with Módulo elástico of 5 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 160 MPa Show Material materials with Resistencia a la flexión of 160 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 120 MPa Show Material materials with Resistencia a la tracción of 120 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 60 kJ/m² | ISO 179/1eU |
23.0 °C | 70 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 8 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1130 J/(kg·K) Show Material materials with Calor específico of 1130 J/(kg·K) | of solid | ||
Coeficiente de dilatación térmica | 23.0 °C | 5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 5E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.3E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 260 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 242 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 242 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | 120mil | |||
Temperatura de fusión | 263 °C Show Material materials with Temperatura de fusión of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 239 °C Show Material materials with Temperatura de reblandecimiento Vicat of 239 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 650 °C, Glow Wire Flammability Index, 80mil: 650 °C, Glow Wire Flammability Index, 120mil: 650 °C, Glow Wire Ignition Temperature, 40mil: 650 °C, Glow Wire Ignition Temperature, 80mil: 650 °C, Glow Wire Ignition Temperature, 120mil: 650 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 22 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 250 V Show Material materials with Índice de seguimiento comparativo of 250 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 13% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |