General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 4.9 % Show Material materials with Absorción de agua of 4.9 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.43 g/cm³ Show Material materials with Densidad of 1.43 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 3.3 % Show Material materials with Elongación of 3.3 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 10.3 GPa Show Material materials with Módulo de flexión of 10.3 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 11.7 GPa Show Material materials with Módulo elástico of 11.7 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 169 MPa Show Material materials with Resistencia a la tracción of 169 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO 179/1eA |
23.0 °C | 23 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 23 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 78 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 78 kJ/m² | ISO 180/1U |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 14 kJ/m² | ISO 180/1A |
23.0 °C | 23 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 23 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2050 J/(kg·K) Show Material materials with Calor específico of 2050 J/(kg·K) | of melt | ||
Heat deflection temperature, 0.45 MPa | 261 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 261 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 215 °C Show Material materials with Temperatura de reblandecimiento Vicat of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, Oxygen index: 27 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 43% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 195°C |