Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 8.5 % Show Material materials with Absorción de agua of 8.5 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.14 g/cm³ Show Material materials with Densidad of 1.14 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 160 MPa Show Material materials with Hardness, Ball Indentation of 160 MPa | ISO 2039-1 |
Límite elástico | 23.0 °C | 82 MPa Show Material materials with Límite elástico of 82 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.8 GPa Show Material materials with Módulo de flexión of 2.8 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.1 GPa Show Material materials with Módulo elástico of 3.1 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5.5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 400 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 400 kJ/m² | No Break @ 23°C, ISO 179/1eU |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 300 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 300 kJ/m² | No Break @ 23°C, ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5.5 kJ/m² | ISO 180/1A |
-30.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5.5 kJ/m² | ISO 180/1A | |
23.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5.5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2790 J/(kg·K) Show Material materials with Calor específico of 2790 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 190 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 190 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 30mil | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 240 °C Show Material materials with Temperatura de reblandecimiento Vicat of 240 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.71 mm, Oxygen index: 28 %, FMVSS Class: DNI - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.5 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.5 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 8E-3 [-] Show Material materials with Dissipation factor, 100Hz of 8E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 32 kV/mm Show Material materials with Rigidez dieléctrica of 32 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |