General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 9.3 GPa Show Material materials with Módulo de flexión of 9.3 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10.5 GPa Show Material materials with Módulo elástico of 10.5 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 280 MPa Show Material materials with Resistencia a la flexión of 280 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -40.0 °C | 75 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 75 kJ/m² | ISO 179/1eU |
23.0 °C | 85 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 85 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 12 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 283 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 283 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 255 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 255 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Temperatura de fusión | 300 °C Show Material materials with Temperatura de fusión of 300 °C | ISO 11357-1/-3 | first heat | |||
Temperatura de transición del vidrio | 115 °C Show Material materials with Temperatura de transición del vidrio of 115 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: SE - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 43 kV/mm Show Material materials with Rigidez dieléctrica of 43 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |