Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.39 g/cm³ Show Material materials with Densidad of 1.39 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 8.9 GPa Show Material materials with Módulo de flexión of 8.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10 GPa Show Material materials with Módulo elástico of 10 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 185 MPa Show Material materials with Resistencia a la tracción of 185 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 70 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 80 kJ/m² | ISO 180/1U |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 11 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 12 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 250 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 250 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 225 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 225 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 255 °C Show Material materials with Temperatura de fusión of 255 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 37 kV/mm Show Material materials with Rigidez dieléctrica of 37 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 33% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |