General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.14 g/cm³ Show Material materials with Densidad of 1.14 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.36 [-] Show Material materials with Coeficiente de Poisson of 0.36 [-] | |
Elongación | 23.0 °C | 14 % Show Material materials with Elongación of 14 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 94 MPa Show Material materials with Límite elástico of 94 MPa | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 3.8 GPa Show Material materials with Módulo elástico of 3.8 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 3 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 78 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 78 °C | ISO 75-1/-2 | |
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C | |