General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.2 % Show Material materials with Elongación of 2.2 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 8.5 GPa Show Material materials with Módulo de flexión of 8.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 8.9 GPa Show Material materials with Módulo elástico of 8.9 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 185 MPa Show Material materials with Resistencia a la flexión of 185 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 109 MPa Show Material materials with Resistencia a la tracción of 109 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA |
-6.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA | |
23.0 °C | 4.6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.6 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 35 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 2000 J/(kg·K) Show Material materials with Calor específico of 2000 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 236 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 236 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 160 °C Show Material materials with Relative temperature index, electrical of 160 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 155 °C Show Material materials with Relative temperature index, mechanical impact of 155 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 190 °C Show Material materials with Relative temperature index, mechanical strength of 190 °C | IEC 60216-1 | 5000 hours | |||
Temperatura de fusión | 267 °C Show Material materials with Temperatura de fusión of 267 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 32 %, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, FMVSS Class: DNI - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 25% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 80°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 2.5s/mm, Ejection temperature: 210°C | |