Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 1.8 % Show Material materials with Absorción de agua of 1.8 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.32 g/cm³ Show Material materials with Densidad of 1.32 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 9 GPa Show Material materials with Módulo de flexión of 9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10 GPa Show Material materials with Módulo elástico of 10 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 250 MPa Show Material materials with Resistencia a la flexión of 250 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 60 kJ/m² | ISO 180/1U |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A |
23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 11 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 2130 J/(kg·K) Show Material materials with Calor específico of 2130 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.6E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.6E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 216 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 216 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 218 °C Show Material materials with Temperatura de fusión of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 725 °C, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 23 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 34 kV/mm Show Material materials with Rigidez dieléctrica of 34 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 6.00E+14 Ω·cm Show Material materials with Volume resistivity of 6.00E+14 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 33% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C | |