Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.68 g/cm³ Show Material materials with Densidad of 1.68 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 1.8 % Show Material materials with Elongación of 1.8 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 17.9 GPa Show Material materials with Módulo de flexión of 17.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 21 GPa Show Material materials with Módulo elástico of 21 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 380 MPa Show Material materials with Resistencia a la flexión of 380 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 260 MPa Show Material materials with Resistencia a la tracción of 260 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | ISO 179/1eA |
23.0 °C | 21 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 21 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 60 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 244 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 244 °C | ISO 75-1/-2 | |
Temperatura de fusión | 296 °C Show Material materials with Temperatura de fusión of 296 °C | ISO 11357-1/-3 | first heat | |
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 725 °C, Glow Wire Flammability Index, 60mil: 725 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 55% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 300°C, Max. melt temperature: 315°C, Min. mold temperature: 70°C, Max. mold temperature: 130°C | |