General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 3 % Show Material materials with Absorción de agua of 3 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.06 g/cm³ Show Material materials with Densidad of 1.06 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |||
Elongación | 23.0 °C | 17 % Show Material materials with Elongación of 17 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 2.1 GPa Show Material materials with Módulo de flexión of 2.1 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Material materials with Módulo elástico of 2.4 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.6E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 218 °C Show Material materials with Temperatura de fusión of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 181 °C Show Material materials with Temperatura de reblandecimiento Vicat of 181 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.86 mm, UL recognition: yes -, FMVSS Class: SE - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 250°C, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C |