General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.12 g/cm³ Show Material materials with Densidad of 1.12 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Material materials with Coeficiente de Poisson of 0.4 [-] | |
Elongación | 23.0 °C | 12 % Show Material materials with Elongación of 12 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 68 MPa Show Material materials with Límite elástico of 68 MPa | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 2.1 GPa Show Material materials with Módulo elástico of 2.1 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 90 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 80°C, Max. mold temperature: 120°C |