General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.47 g/cm³ Show Material materials with Densidad of 1.47 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 2.3 % Show Material materials with Elongación of 2.3 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 310 MPa Show Material materials with Hardness, Ball Indentation of 310 MPa | ISO 2039-1 |
Módulo de flexión | 23.0 °C | 10.5 GPa Show Material materials with Módulo de flexión of 10.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 12 GPa Show Material materials with Módulo elástico of 12 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 5.5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 276 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 276 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 262 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 262 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 300 °C Show Material materials with Temperatura de fusión of 300 °C | ISO 11357-1/-3 | first heat | |||
Temperatura de transición del vidrio | 135 °C Show Material materials with Temperatura de transición del vidrio of 135 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 28 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 34 kV/mm Show Material materials with Rigidez dieléctrica of 34 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C | |