Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 1.5 % Show Material materials with Absorción de agua of 1.5 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.05 g/cm³ Show Material materials with Densidad of 1.05 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.46 [-] Show Material materials with Coeficiente de Poisson of 0.46 [-] | |||
Elongación | 23.0 °C | 230 % Show Material materials with Elongación of 230 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 32 % Show Material materials with Elongation at yield of 32 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 38 MPa Show Material materials with Límite elástico of 38 MPa | ISO 527-1/-2 | ||
Módulo elástico | 23.0 °C | 0.79 GPa Show Material materials with Módulo elástico of 0.79 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 24 MPa Show Material materials with Resistencia a la flexión of 24 MPa | ISO 178 | ||
Resistencia a la tracción | 23.0 °C | 38 MPa Show Material materials with Resistencia a la tracción of 38 MPa | ISO 527-1/-2 | 50mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | ||
23.0 °C | 24 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 24 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 24 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 24 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 110 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 110 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 46 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 46 °C | ISO 75-1/-2 | |
Temperatura de fusión | 197 °C Show Material materials with Temperatura de fusión of 197 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.6 % Show Material materials with Contracción of 1.6 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1 % Show Material materials with Contracción transversal of 1 % | ISO 294-4, 2577 |
Melt viscosity | 250.0 °C | 210 Pa·s Show Material materials with Melt viscosity of 210 Pa·s | ISO 11443 | @ 1000 sec-1, 250°C |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 230°C, Min. melt temperature: 225°C, Max. melt temperature: 235°C, Mold Temperature Optimum: 55°C, Min. mold temperature: 50°C, Max. mold temperature: 80°C | |