General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.65 g/cm³ Show Material materials with Densidad of 1.65 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 1.6 % Show Material materials with Elongación of 1.6 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 16.6 GPa Show Material materials with Módulo de flexión of 16.6 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 18 GPa Show Material materials with Módulo elástico of 18 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 305 MPa Show Material materials with Resistencia a la flexión of 305 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 217 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 217 °C | ISO 75-1/-2 | |
Temperatura de fusión | 298 °C Show Material materials with Temperatura de fusión of 298 °C | ISO 11357-1/-3 | first heat | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 50% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 300°C, Max. melt temperature: 315°C, Min. mold temperature: 70°C, Max. mold temperature: 130°C |