General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 1.05 g/cm³ Show Material materials with Densidad of 1.05 g/cm³ |
Densidad relativa | 23.0 °C | 1.05 [-] Show Material materials with Densidad relativa of 1.05 [-] |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 63 [-] Show Material materials with Dureza Shore D of 63 [-] | |
Elongación | -40.0 °C | 220 % Show Material materials with Elongación of 220 % | |
23.0 °C | 380 % Show Material materials with Elongación of 380 % | ||
80.0 °C | 420 % Show Material materials with Elongación of 420 % | ||
Elongation at yield | 23.0 °C | 26 % Show Material materials with Elongation at yield of 26 % | |
Hardness, Rockwell R | 23.0 °C | 75 [-] Show Material materials with Hardness, Rockwell R of 75 [-] | |
Límite elástico | 23.0 °C | 21 MPa Show Material materials with Límite elástico of 21 MPa | |
Módulo de flexión | -40.0 °C | 2.28 GPa Show Material materials with Módulo de flexión of 2.28 GPa | |
23.0 °C | 0.31 GPa Show Material materials with Módulo de flexión of 0.31 GPa | ||
80.0 °C | 0.16 GPa Show Material materials with Módulo de flexión of 0.16 GPa | ||
Resistencia a la tracción | -40.0 °C | 76 MPa Show Material materials with Resistencia a la tracción of 76 MPa | |
23.0 °C | 62 MPa Show Material materials with Resistencia a la tracción of 62 MPa | ||
80.0 °C | 54 MPa Show Material materials with Resistencia a la tracción of 54 MPa | ||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 21 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 21 kJ/m² | No Break @ 23,80°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor latente de fusión | 39 J/g Show Material materials with Calor latente de fusión of 39 J/g | 24% crystallinity | |
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-4 1/K | for -30 to 50°C |
Conductividad térmica | 23.0 °C | 0.19 W/(m·K) Show Material materials with Conductividad térmica of 0.19 W/(m·K) | |
Temperatura de flexión bajo carga | 39.85 °C Show Material materials with Temperatura de flexión bajo carga of 39.85 °C | ||
Temperatura de fusión | 183.85 °C Show Material materials with Temperatura de fusión of 183.85 °C | ||
Temperatura de transición del vidrio | 41.85 °C Show Material materials with Temperatura de transición del vidrio of 41.85 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.1 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.1 [-] | Dry |
Dissipation factor, 1MHz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 1MHz of 0.04 [-] | Dry |
Rigidez dieléctrica | 23.0 °C | 24 kV/mm Show Material materials with Rigidez dieléctrica of 24 kV/mm |
Technological properties
Property | ||
---|---|---|
Application areas | Tubing, hoses, and pipes for automotive, trucking, industrial, and petroleum production applications. Examples are heavy truck airbrake tubing, automotive fuel lines, and submarine flexible pipes for offshore oil production. Thermoplastic powder coatings for industrial, transportation, and retail items are prepared in a Nylon 11 base. Nylon 11 is being used in a variety of food-contact applications, including sausage casing, beverage tubing, and reusable kitchen devices. |