General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 1.06 - 1.16 g/cm³ Show Material materials with Densidad of 1.06 - 1.16 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Rockwell M | 23.0 °C | 78 [-] Show Material materials with Dureza Rockwell M of 78 [-] | |
Impact strength, Izod notched, ASTM | -40.15 °C | 53 J/m Show Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D256 |
22.85 °C | 64 J/m Show Material materials with Impact strength, Izod notched, ASTM of 64 J/m | ASTM D256 | |
92.85 °C | 91 J/m Show Material materials with Impact strength, Izod notched, ASTM of 91 J/m | ASTM D256 | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2000 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2000 J/m | min., ASTM D256 |
Límite elástico | 22.85 °C | 80 MPa Show Material materials with Límite elástico of 80 MPa | |
92.85 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ||
Módulo de cizallamiento | 23.0 °C | 2.69 GPa Show Material materials with Módulo de cizallamiento of 2.69 GPa | ASTM D638 |
93.0 °C | 2.48 GPa Show Material materials with Módulo de cizallamiento of 2.48 GPa | ASTM D638 | |
Módulo de flexión | -17.15 °C | 2.65 GPa Show Material materials with Módulo de flexión of 2.65 GPa | ASTM D790 |
22.85 °C | 2.59 GPa Show Material materials with Módulo de flexión of 2.59 GPa | ASTM D790 | |
92.85 °C | 2.48 GPa Show Material materials with Módulo de flexión of 2.48 GPa | ASTM D790 | |
Módulo elástico | 22.85 °C | 2.69 GPa Show Material materials with Módulo elástico of 2.69 GPa | ASTM D638 |
92.85 °C | 2.48 GPa Show Material materials with Módulo elástico of 2.48 GPa | ASTM D638 | |
Resistencia a la flexión | -10.15 °C | 2.65 MPa Show Material materials with Resistencia a la flexión of 2.65 MPa | ASTM D790 |
22.85 °C | 2.59 MPa Show Material materials with Resistencia a la flexión of 2.59 MPa | ASTM D790 | |
92.85 °C | 2.48 MPa Show Material materials with Resistencia a la flexión of 2.48 MPa | ASTM D790 | |
Resistencia al cizallamiento | 23.0 °C | 76 MPa Show Material materials with Resistencia al cizallamiento of 76 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 5.2E-5 1/K |
Temperatura de flexión bajo carga | 178.85 °C Show Material materials with Temperatura de flexión bajo carga of 178.85 °C | |
Temperatura de fusión | 535 - 540 °C Show Material materials with Temperatura de fusión of 535 - 540 °C | |
Temperatura de transición del vidrio | 480 - 498 °C Show Material materials with Temperatura de transición del vidrio of 480 - 498 °C |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive, business machine, and electrical/electronics industries. PPO is mainly used to manufacture blends with high-impact polystyrene (HIPS). PPO/nylon, PPO/PBT, and PPO/polyolefin blends are also available on the market. PPO based materials ranking first in terms of total consumption among blends based on engineering resins such as nylon, polycarbonate (PC), polyacetal, and reinforced terephthalate polyesters (PET and PBT). |