General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.03 % Show Material materials with Absorción de agua of 0.03 % | |
Densidad | 23.0 °C | 1.6 - 1.8 g/cm³ Show Material materials with Densidad of 1.6 - 1.8 g/cm³ | observed density |
Mecánica
Property | Temperature | Value |
---|---|---|
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] |
Impact strength, Izod notched, ASTM | 23.0 °C | 32 J/m Show Material materials with Impact strength, Izod notched, ASTM of 32 J/m |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 101 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 101 J/m |
Límite elástico | 23.0 °C | 74 MPa Show Material materials with Límite elástico of 74 MPa |
Módulo de flexión | 23.0 °C | 15.2 GPa Show Material materials with Módulo de flexión of 15.2 GPa |
Resistencia a la compresión | 23.0 °C | 110 MPa Show Material materials with Resistencia a la compresión of 110 MPa |
Resistencia a la flexión | 23.0 °C | 100 MPa Show Material materials with Resistencia a la flexión of 100 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.8E-5 1/K | |||
Conductividad térmica | 23.0 °C | 0.29 W/(m·K) Show Material materials with Conductividad térmica of 0.29 W/(m·K) | |||
Temperatura de flexión bajo carga | 259.85 °C Show Material materials with Temperatura de flexión bajo carga of 259.85 °C | min. | |||
Temperatura de fusión | 284.85 °C Show Material materials with Temperatura de fusión of 284.85 °C | DSC | |||
Temperatura de transición del vidrio | 84.85 °C Show Material materials with Temperatura de transición del vidrio of 84.85 °C | DSC | |||
Inflamabilidad | V-0/5V |
Eléctrico
Property | Temperature | Value |
---|---|---|
Constante dieléctrica | 23.0 °C | 4.6 [-] Show Material materials with Constante dieléctrica of 4.6 [-] |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] |
Resistividad eléctrica | 23.0 °C | 2.00E+14 Ω·m Show Material materials with Resistividad eléctrica of 2.00E+14 Ω·m |
Rigidez dieléctrica | 23.0 °C | 13.4 - 15.7 kV/mm Show Material materials with Rigidez dieléctrica of 13.4 - 15.7 kV/mm |
Índice de seguimiento comparativo | 23.0 °C | 235 V Show Material materials with Índice de seguimiento comparativo of 235 V |
Technological properties
Property | ||
---|---|---|
Application areas | Poly( p-phenylene sulfide) (PPS) is mainly used in the reinforced form with glass fiber or mineral fillers as a high-performance thermoplastic. It is used for electrical and electronic parts (e.g., plugs and multipoint connectors, bobbins, relays, switches, encapsulation of electronic component, etc.), automobile parts (air intake systems, pumps, valves, gaskets, components for exhaust gas recirculation systems, etc.), and as components for mechanical and precision engineering. Nonfiller PPS is used for fiber, film, sheet, nonwoven fabric, etc. | |
Fillers | Glass Fiber and Mineral Powder |