General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.24 % Show Material materials with Absorción de agua of 0.24 % | ASTM D570, 24h, for Immersion 48h at 50°C: 0.72% |
Coefficient of friction | 0.29 [-] Show Material materials with Coefficient of friction of 0.29 [-] | Steady state, unlubricated in air (PV=0875 MPa*m*s⁻¹), for static in air: 0.35 | |
Densidad | 23.0 °C | 1.43 g/cm³ Show Material materials with Densidad of 1.43 g/cm³ | ASTM D792 |
Índice límite de óxigeno | 23.0 °C | 53 % Show Material materials with Índice límite de óxigeno of 53 % | ASTM D2863 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.41 [-] Show Material materials with Coeficiente de Poisson of 0.41 [-] | |
Dureza Rockwell M | 23.0 °C | 92 - 102 [-] Show Material materials with Dureza Rockwell M of 92 - 102 [-] | ASTM D785 |
Elongación | 23.0 °C | 7.5 % Show Material materials with Elongación of 7.5 % | ASTM D1708 |
260.0 °C | 6 % Show Material materials with Elongación of 6 % | ASTM D1708 | |
Hardness, Rockwell E | 23.0 °C | 45 - 60 [-] Show Material materials with Hardness, Rockwell E of 45 - 60 [-] | ASTM D785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 42.7 J/m Show Material materials with Impact strength, Izod notched, ASTM of 42.7 J/m | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 747 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 747 J/m | |
Módulo de compresión | 23.0 °C | 2413 MPa Show Material materials with Módulo de compresión of 2413 MPa | ASTM D695 |
Módulo de flexión | 23.0 °C | 3.1 GPa Show Material materials with Módulo de flexión of 3.1 GPa | ASTM D790 |
260.0 °C | 1.72 GPa Show Material materials with Módulo de flexión of 1.72 GPa | ASTM D790 | |
Resistencia a la compresión | 23.0 °C | 24.8 MPa Show Material materials with Resistencia a la compresión of 24.8 MPa | ASTM D695, 1% strain, for 10% strain: 133.1 MPa |
Resistencia a la flexión | 23.0 °C | 110.3 MPa Show Material materials with Resistencia a la flexión of 110.3 MPa | |
260.0 °C | 62.1 MPa Show Material materials with Resistencia a la flexión of 62.1 MPa | ||
Resistencia a la tracción | 23.0 °C | 86.2 MPa Show Material materials with Resistencia a la tracción of 86.2 MPa | ASTM D1708 |
260.0 °C | 41.4 MPa Show Material materials with Resistencia a la tracción of 41.4 MPa | ASTM D1708 | |
Resistencia al cizallamiento | 23.0 °C | 89.6 MPa Show Material materials with Resistencia al cizallamiento of 89.6 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 1130 J/(kg·K) Show Material materials with Calor específico of 1130 J/(kg·K) | |
Coeficiente de dilatación térmica | 23.0 °C | 5.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 5.4E-5 1/K | ASTM D696, @23-300°C, 45*10⁻⁶ K⁻¹@-62 to 23°C |
Conductividad térmica | 40.0 °C | 0.35 W/(m·K) Show Material materials with Conductividad térmica of 0.35 W/(m·K) | |
Heat deflection temperature, 1.80 MPa | 359.85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 359.85 °C | ASTM D648 | |
Temperatura de transición del vidrio | 359.85 - 409.85 °C Show Material materials with Temperatura de transición del vidrio of 359.85 - 409.85 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.55 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.55 [-] | ASTM D150 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.62 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.62 [-] | ASTM D150 |
Dissipation factor, 100Hz | 23.0 °C | 1.8E-3 [-] Show Material materials with Dissipation factor, 100Hz of 1.8E-3 [-] | ASTM D150 |
Dissipation factor, 1MHz | 23.0 °C | 3.4E-3 [-] Show Material materials with Dissipation factor, 1MHz of 3.4E-3 [-] | ASTM D150 |
Factor de disipación | 23.0 °C | 3.6E-3 [-] Show Material materials with Factor de disipación of 3.6E-3 [-] | ASTM D150, 10000 Hz |
Resistividad eléctrica | 23.0 °C | 1.00E+14 - 1.00E+15 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+14 - 1.00E+15 Ω·m | ASTM D257 |
Rigidez dieléctrica | 23.0 °C | 0.02 kV/mm Show Material materials with Rigidez dieléctrica of 0.02 kV/mm | ASTM D149, short time, 0.002m thick |
Surface resistivity | 23.0 °C | 1.00E+15 - 1.00E+16 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 - 1.00E+16 Ω/sq | ASTM D257 |
Technological properties
Property | ||
---|---|---|
Application areas | Vespel molded parts are used in automobiles, large on-and-off-road vehicles, farm equipment, business machines, electronic equipment, etc.: rotary seal rings, thrust washers and discs, bushings, flanges bearings, printer platen bars, plungers, printer wireguides, stripper fingers, spline couplings, wear strips, locknut inserts, valve seats, check valve balls, thermal and electrical insulators. |