Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 23.0 °C | 277 - 354 [-] Show Material materials with Dureza Brinell of 277 - 354 [-] |
Elongación | 23.0 °C | 17 % Show Material materials with Elongación of 17 % |
Límite elástico Rp 0,2 | 23.0 °C | 827 MPa Show Material materials with Límite elástico Rp 0,2 of 827 MPa |
Resistencia a la tracción | 23.0 °C | 1034 MPa Show Material materials with Resistencia a la tracción of 1034 MPa |
Chemical properties
Property | Value |
---|---|
Aluminio | 0.5 % Show Material materials with Aluminio of 0.5 % |
Cromo | 19 % Show Material materials with Cromo of 19 % |
Hierro | 18 - 18.5 % Show Material materials with Hierro of 18 - 18.5 % |
Molibdeno | 3 % Show Material materials with Molibdeno of 3 % |
Niobio | 5 % Show Material materials with Niobio of 5 % |
Níquel | 53 % Show Material materials with Níquel of 53 % |
Titanio | 0.9 % Show Material materials with Titanio of 0.9 % |
Technological properties
Property | ||
---|---|---|
Application areas | Offshore & marine: Fasteners, valves, choke stems, down-hole tooling, cryogenic storage tanks and pump bodies;Aerospace: Jet engine components, rocket motors and thrust reversers;Power generation: Nuclear reactor parts, gas turbine components, nuclear fuel element spacers, containment vessels and valves;Other: Hot extrusion tooling | |
Cold Forming | It can be cold worked while in the solution treated condition due to its high elongation. | |
Corrosion properties | Excellent corrosion resistance | |
General machinability | Readily machined in the solution treated condition but the material’s high strength and work-hardening characteristics should be taken into account. | |
Hot forming | It can be hot worked between 985-1150°C. |