General
Property | Value |
---|---|
Bio-based content | 100 % Show Material materials with Bio-based content of 100 % |
Densidad | 1.05 g/cm³ Show Material materials with Densidad of 1.05 g/cm³ |
Mecánica
Property | Value |
---|---|
Dureza Shore D | 64.0 [-] Show Material materials with Dureza Shore D of 64.0 [-] |
Elongación | 29.0 % Show Material materials with Elongación of 29.0 % |
Impact strength, Izod unnotched, ASTM | 220.0 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 220.0 J/m |
Módulo de flexión | 0.7 GPa Show Material materials with Módulo de flexión of 0.7 GPa |
Resistencia a la flexión | 9.0 MPa Show Material materials with Resistencia a la flexión of 9.0 MPa |
Resistencia a la tracción | 16 MPa Show Material materials with Resistencia a la tracción of 16 MPa |
Aplicaciones térmicas
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 20 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 20 g/10min | 175°C/5 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Bottle cap, closure, high impact bin, container, pails. | |
Certifications | Food Contact: Halal | |
Processing methods | 1. Clean extruder with general purpose polyethylene or polypropylene. 2. Vacuum out hopper system to avoid contamination and make sure that the humidity of the air is below 40°C at dew point. 3. Introduce ICBP Bio Resin in to the extruder at the operating conditions used in the first step. 4. Once ICBP Bio Resin has been purged, reduce barrel temperatures to desired set points. 5. At shutdown, purge machine with PE or PP. |