General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 120.0 °C | 4 - 5 % Show Material materials with Contracción of 4 - 5 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Contracción transversal | 120.0 °C | 2 % Show Material materials with Contracción transversal of 2 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Densidad | 20.0 °C | 0.91 g/cm³ Show Material materials with Densidad of 0.91 g/cm³ | |
Densidad superficial | 20.0 °C | 1.36E-3 - 3.18E-3 g/cm² Show Material materials with Densidad superficial of 1.36E-3 - 3.18E-3 g/cm² | |
Elasticidad de la película | 20.0 °C | 31.4 - 73.26 m²/kg Show Material materials with Elasticidad de la película of 31.4 - 73.26 m²/kg |
Medidas
| Property | Value |
|---|---|
Espesor | 0.02 - 0.04 mm Show Material materials with Espesor of 0.02 - 0.04 mm |
Dimensions | Available thicknesses: 15, 20, 25, 30, 35µm. |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 20.0 °C | 200 % Show Material materials with Elongación of 200 % | GOST 14236, ISO 527, ASTM D882 |
Elongación transversal | 20.0 °C | 70 % Show Material materials with Elongación transversal of 70 % | GOST 14236, ISO 527, ASTM D882 |
Resistencia a la tracción | 20.0 °C | 140 - 150 MPa Show Material materials with Resistencia a la tracción of 140 - 150 MPa | GOST 14236, ISO 527, ASTM D882 |
Resistencia a la tracción transversal | 20.0 °C | 250 MPa Show Material materials with Resistencia a la tracción transversal of 250 MPa | GOST 14236, ISO 527, ASTM D882 |
Óptico
| Property | Value | Comment |
|---|---|---|
Turbidez | 2 % Show Material materials with Turbidez of 2 % | GOST 15875, ISO 14782, ASTM D 1003 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High quality rotogravure and flexographic solvent printing; solvent or solventless polyurethane laminating adhesives; for the production of flexible packaging (typically duplex) with frame cold seal glue. | |
| Friction | Kinetic coefficient of friction µ= 0.1-0.35 (GOST 27492, ISO 8295, ASTM D 1894). | |
| Other | PGR BOPP films comprise: A treated modified copolymer skin layer, a transparent oriented polypropylene core layer, a non-heat-sealable, untreated release skin layer with low coefficient of friction. | |
| Processing history | Treatment level: 38 mN/m (ISO 8296, ASTM D 2578). | |