Propiedades
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Densidad | 20.0 °C | 4.43 g/cm³ Show Material materials with Densidad of 4.43 g/cm³ | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coeficiente de Poisson | -269.0 °C | 0.311 [-] Show Material materials with Coeficiente de Poisson of 0.311 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 0.327 [-] Show Material materials with Coeficiente de Poisson of 0.327 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 0.333 [-] Show Material materials with Coeficiente de Poisson of 0.333 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Dureza Brinell | 20.0 °C | 310.0 Show Material materials with Dureza Brinell of 310.0 | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod |
Elongación | 20.0 °C | 8.0 % Show Material materials with Elongación of 8.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
Estricción | 20.0 °C | 15.0 % Show Material materials with Estricción of 15.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
20.0 °C | 20.0 % Show Material materials with Estricción of 20.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging | |
Módulo de cizallamiento | 20.0 °C | 43.0 GPa Show Material materials with Módulo de cizallamiento of 43.0 GPa | Artificially Aged | WL 3.7164-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Forging, Rod |
Módulo elástico | -269.0 °C | 119.6 GPa Show Material materials with Módulo elástico of 119.6 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 118.2 GPa Show Material materials with Módulo elástico of 118.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
20.0 °C | 110.0 GPa Show Material materials with Módulo elástico of 110.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 109.2 GPa Show Material materials with Módulo elástico of 109.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
200.0 °C | 98.0 GPa Show Material materials with Módulo elástico of 98.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
400.0 °C | 84.0 GPa Show Material materials with Módulo elástico of 84.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Resistencia a la tracción | 20.0 °C | 1060.0 MPa Show Material materials with Resistencia a la tracción of 1060.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging |
20.0 °C | 1070.0 MPa Show Material materials with Resistencia a la tracción of 1070.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging | |
20.0 °C | 1100.0 MPa Show Material materials with Resistencia a la tracción of 1100.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging, Rod | |
20.0 °C | 1180.0 MPa Show Material materials with Resistencia a la tracción of 1180.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
100.0 °C | 1090.0 MPa Show Material materials with Resistencia a la tracción of 1090.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
200.0 °C | 1000.0 MPa Show Material materials with Resistencia a la tracción of 1000.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
300.0 °C | 910.0 MPa Show Material materials with Resistencia a la tracción of 910.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
400.0 °C | 855.0 MPa Show Material materials with Resistencia a la tracción of 855.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
500.0 °C | 735.0 MPa Show Material materials with Resistencia a la tracción of 735.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Calor específico | 370.0 - 674.0 J/(kg·K) Show Material materials with Calor específico of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Coeficiente de dilatación térmica | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Conductividad térmica | 20.0 °C | 7.12 W/(m·K) Show Material materials with Conductividad térmica of 7.12 W/(m·K) | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Temperatura de fusión | 1500.0 - 1750.0 °C Show Material materials with Temperatura de fusión of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy |
Eléctrico
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Resistividad eléctrica | 20.0 °C | 1.71e-06 Ω·m Show Material materials with Resistividad eléctrica of 1.71e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminio | 5.5 - 6.75 % Show Material materials with Aluminio of 5.5 - 6.75 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Carbono | 0.08 Show Material materials with Carbono of 0.08 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Hidrógeno | 0.015 Show Material materials with Hidrógeno of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Hierro | 0.3 Show Material materials with Hierro of 0.3 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Nitrógeno | 0.05 Show Material materials with Nitrógeno of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Oxígeno | 0.2 Show Material materials with Oxígeno of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Titanio | 87.7 % Show Material materials with Titanio of 87.7 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Vanadio | 3.5 - 4.5 % Show Material materials with Vanadio of 3.5 - 4.5 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |