EN 12166 Grade CuZn40Pb2 H075

Want to keep this datasheet? Save it now in your required format

Description

Material CuZn40Pb2, mat. No. CW617N, is an unhardenable wrought alloy. to the comparable make CuZn40Pb2, mat. No. 2.0402 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn40. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: for hot-pressed components, turned parts for precision engineering and optics, circuit boards and clockwerks as well as for clamps for electrical engineering.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

Properties of Copper

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value
Densidad	20.0 °C	8.4 - 8.44 g/cm³ Show Material materials with Densidad of 8.4 - 8.44 g/cm³

Mecánica

Property	Temperature	Value	Comment
Dureza Brinell	20.0 °C	75 [-] Show Material materials with Dureza Brinell of 75 [-]
Dureza Vickers	20.0 °C	80 [-] Show Material materials with Dureza Vickers of 80 [-]
Elongación	20.0 °C	20 % Show Material materials with Elongación of 20 %
Límite elástico Rp 0,2	20.0 °C	110 - 120 MPa Show Material materials with Límite elástico Rp 0,2 of 110 - 120 MPa
Límite elástico Rp 1,0	20.0 °C	140 MPa Show Material materials with Límite elástico Rp 1,0 of 140 MPa
	50.0 °C	140 MPa Show Material materials with Límite elástico Rp 1,0 of 140 MPa
	100.0 °C	137 MPa Show Material materials with Límite elástico Rp 1,0 of 137 MPa
	150.0 °C	137 MPa Show Material materials with Límite elástico Rp 1,0 of 137 MPa
	200.0 °C	132 MPa Show Material materials with Límite elástico Rp 1,0 of 132 MPa

Módulo de cizallamiento	23.0 °C	40 GPa Show Material materials with Módulo de cizallamiento of 40 GPa	Typical for Wrought Copper Brass
Módulo elástico	-195.0 °C	108 GPa Show Material materials with Módulo elástico of 108 GPa
	-100.0 °C	106 GPa Show Material materials with Módulo elástico of 106 GPa
	20.0 °C	96 - 105 GPa Show Material materials with Módulo elástico of 96 - 105 GPa
	50.0 °C	100 GPa Show Material materials with Módulo elástico of 100 GPa
	100.0 °C	93 GPa Show Material materials with Módulo elástico of 93 GPa
	150.0 °C	91 GPa Show Material materials with Módulo elástico of 91 GPa
	200.0 °C	89 GPa Show Material materials with Módulo elástico of 89 GPa
	250.0 °C	83 GPa Show Material materials with Módulo elástico of 83 GPa
	Unlock all property charts
Resistencia a la tracción	20.0 °C	340 MPa Show Material materials with Resistencia a la tracción of 340 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	20.0 °C	377 J/(kg·K) Show Material materials with Calor específico of 377 J/(kg·K)
Coeficiente de dilatación térmica	100.0 °C	2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-5 1/K
	300.0 °C	2.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1E-5 1/K
	Unlock all property charts
Conductividad térmica	-200.0 °C	50 W/(m·K) Show Material materials with Conductividad térmica of 50 W/(m·K)
	20.0 °C	113 - 123 W/(m·K) Show Material materials with Conductividad térmica of 113 - 123 W/(m·K)
	Unlock all property charts
Temperatura de fusión		875 - 1075 °C Show Material materials with Temperatura de fusión of 875 - 1075 °C	Typical for Wrought Copper Brass

Eléctrico

Property	Temperature	Value
Conductividad eléctrica	20.0 °C	1.49E+7 - 1.50E+7 S/m Show Material materials with Conductividad eléctrica of 1.49E+7 - 1.50E+7 S/m
	200.0 °C	1.20E+7 S/m Show Material materials with Conductividad eléctrica of 1.20E+7 S/m
	Unlock all property charts
Resistividad eléctrica	20.0 °C	6.6E-8 Ω·m Show Material materials with Resistividad eléctrica of 6.6E-8 Ω·m
	200.0 °C	8.3E-8 Ω·m Show Material materials with Resistividad eléctrica of 8.3E-8 Ω·m
	Unlock all property charts
Specific Electrical conductivity		25 - 25.7 % IACS Show Material materials with Specific Electrical conductivity of 25 - 25.7 % IACS

Chemical properties

Property	Value
Aluminio	0.05 % Show Material materials with Aluminio of 0.05 %
Cobre	57 - 59 % Show Material materials with Cobre of 57 - 59 %
Estaño	0.3 % Show Material materials with Estaño of 0.3 %
Hierro	0.3 % Show Material materials with Hierro of 0.3 %
Níquel	0.3 % Show Material materials with Níquel of 0.3 %
Plomo	1.6 - 2.5 % Show Material materials with Plomo of 1.6 - 2.5 %

Looking for suppliers of this material? Click to see 17 supplier of EN 12166 Grade CuZn40Pb2 H075 on Matmatch