Propiedades
General
| Property | Value | Condition |
|---|---|---|
Densidad | 2.78 g/cm³ Show Material materials with Densidad of 2.78 g/cm³ | T651 |
3.0 g/cm³ Show Material materials with Densidad of 3.0 g/cm³ | T651 |
Mecánica
| Property | Temperature | Value | Condition | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Elongación | -195 °C | 11 % Show Material materials with Elongación of 11 % | T651 | Elongation in 50 mm |
-80 °C | 10 % Show Material materials with Elongación of 10 % | T651 | Elongation in 50 mm | |
4.6 % Show Material materials with Elongación of 4.6 % | T651 | |||
0 °C | 10 % Show Material materials with Elongación of 10 % | T651 | Elongation in 50 mm | |
24 °C | 10 % Show Material materials with Elongación of 10 % | T651 | Elongation in 50 mm | |
100 °C | 10 % Show Material materials with Elongación of 10 % | T651 | Elongation in 50 mm | |
150 °C | 17 % Show Material materials with Elongación of 17 % | T651 | Elongation in 50 mm | |
205 °C | 27 % Show Material materials with Elongación of 27 % | T651 | Elongation in 50 mm | |
260 °C | 55 % Show Material materials with Elongación of 55 % | T651 | Elongation in 50 mm | |
315 °C | 75 % Show Material materials with Elongación of 75 % | T651 | Elongation in 50 mm | |
370 °C | 100 % Show Material materials with Elongación of 100 % | T651 | Elongation in 50 mm | |
Límite elástico | -195 °C | 469 MPa Show Material materials with Límite elástico of 469 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
-80 °C | 407 MPa Show Material materials with Límite elástico of 407 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
360.0 MPa Show Material materials with Límite elástico of 360.0 MPa | T651 | |||
0 °C | 400 MPa Show Material materials with Límite elástico of 400 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
24 °C | 393 MPa Show Material materials with Límite elástico of 393 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
100 °C | 372 MPa Show Material materials with Límite elástico of 372 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
150 °C | 248 MPa Show Material materials with Límite elástico of 248 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
205 °C | 131 MPa Show Material materials with Límite elástico of 131 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
260 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
315 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
370 °C | 28 MPa Show Material materials with Límite elástico of 28 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
Módulo de cizallamiento | 28.0 GPa Show Material materials with Módulo de cizallamiento of 28.0 GPa | T651 | ||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T651 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | -195 °C | 580 MPa Show Material materials with Resistencia a la tracción of 580 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
-80 °C | 495 MPa Show Material materials with Resistencia a la tracción of 495 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
0 °C | 483 MPa Show Material materials with Resistencia a la tracción of 483 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
490.0 MPa Show Material materials with Resistencia a la tracción of 490.0 MPa | T651 | |||
24 °C | 475 MPa Show Material materials with Resistencia a la tracción of 475 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
100 °C | 448 MPa Show Material materials with Resistencia a la tracción of 448 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
150 °C | 310 MPa Show Material materials with Resistencia a la tracción of 310 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
205 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
260 °C | 75 MPa Show Material materials with Resistencia a la tracción of 75 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Aplicaciones térmicas
| Property | Value | Condition |
|---|---|---|
Calor específico | 870.0 J/(kg·K) Show Material materials with Calor específico of 870.0 J/(kg·K) | T651 |
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T651 |
Conductividad térmica | 120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | T651 |
Temperatura de fusión | 500.0 °C Show Material materials with Temperatura de fusión of 500.0 °C | T651 |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 18000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Resistividad eléctrica | 3.4e-08 - 6e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition |
|---|---|---|
Aluminio | 90.7 - 94.7 % Show Material materials with Aluminio of 90.7 - 94.7 % | T651 |
Circonio | 0.2 % Show Material materials with Circonio of 0.2 % | T651 |
Cobre | 3.8 - 4.9 % Show Material materials with Cobre of 3.8 - 4.9 % | T651 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T651 |
Hierro | 0.5 % Show Material materials with Hierro of 0.5 % | T651 |
Magnesio | 1.2 - 1.8 % Show Material materials with Magnesio of 1.2 - 1.8 % | T651 |
Manganeso | 0.3 - 0.9 % Show Material materials with Manganeso of 0.3 - 0.9 % | T651 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T651 |
Silicona | 0.5 % Show Material materials with Silicona of 0.5 % | T651 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T651 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |