General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 7.8 g/cm³ Show Material materials with Densidad of 7.8 g/cm³ |
Medidas
Property | Value |
---|---|
Diámetro | 25.4 - 140 mm Show Material materials with Diámetro of 25.4 - 140 mm |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 23.0 °C | 230 J Show Material materials with Charpy impact energy, V-notch of 230 J | |
Coeficiente de Poisson | 23.0 °C | 0.3 [-] Show Material materials with Coeficiente de Poisson of 0.3 [-] | Typical for Austenitic Stainless Steel |
Dureza Brinell | 23.0 °C | 201 - 293 [-] Show Material materials with Dureza Brinell of 201 - 293 [-] | |
Elongación | 23.0 °C | 35 - 40 % Show Material materials with Elongación of 35 - 40 % | |
Límite elástico | 23.0 °C | 440 MPa Show Material materials with Límite elástico of 440 MPa | |
Límite elástico Rp 0,2 | 23.0 °C | 345 - 420 MPa Show Material materials with Límite elástico Rp 0,2 of 345 - 420 MPa | |
Módulo de cizallamiento | 23.0 °C | 77 GPa Show Material materials with Módulo de cizallamiento of 77 GPa | Typical for Austenitic Stainless Steel |
Módulo elástico | 23.0 °C | 220 GPa Show Material materials with Módulo elástico of 220 GPa | |
Resistencia a la tracción | 23.0 °C | 655 - 790 MPa Show Material materials with Resistencia a la tracción of 655 - 790 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 480 J/(kg·K) Show Material materials with Calor específico of 480 J/(kg·K) | |
Coeficiente de dilatación térmica | 23.0 °C | 1.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-5 1/K | |
Conductividad térmica | 23.0 °C | 13 W/(m·K) Show Material materials with Conductividad térmica of 13 W/(m·K) | |
Temperatura de fusión | 1230 - 1480 °C Show Material materials with Temperatura de fusión of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Resistividad eléctrica | 23.0 °C | 8.5E-7 Ω·m Show Material materials with Resistividad eléctrica of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
Property | Value | Comment |
---|---|---|
Azufre | 0 - 0.03 % Show Material materials with Azufre of 0 - 0.03 % | |
Carbono | 0 - 0.06 % Show Material materials with Carbono of 0 - 0.06 % | |
Cromo | 20.5 - 23.5 % Show Material materials with Cromo of 20.5 - 23.5 % | |
Fósforo | 0 - 0.04 % Show Material materials with Fósforo of 0 - 0.04 % | |
Hierro | 52.1 - 62.1 % Show Material materials with Hierro of 52.1 - 62.1 % | Balance |
Manganeso | 4 - 6 % Show Material materials with Manganeso of 4 - 6 % | |
Molibdeno | 1.5 - 3 % Show Material materials with Molibdeno of 1.5 - 3 % | |
Niobio | 0.1 - 0.3 % Show Material materials with Niobio of 0.1 - 0.3 % | |
Nitrógeno | 0.2 - 0.4 % Show Material materials with Nitrógeno of 0.2 - 0.4 % | |
Níquel | 11.5 - 13.5 % Show Material materials with Níquel of 11.5 - 13.5 % | |
Silicona | 0 - 1 % Show Material materials with Silicona of 0 - 1 % | |
Vanadio | 0.1 - 0.3 % Show Material materials with Vanadio of 0.1 - 0.3 % |
Technological properties
Property | ||
---|---|---|
Application areas | The combination of corrosion resistance and mechanical strength is utilized in marine hardware, pump shafting, petrochemical, pulp & Equipment for the Paper Industry, Paper Industry, food processing and petroleum industries. Can also be used in “down hole” applications due to sulfide stress cracking resistance. NITRONIC® 50 in both the annealed and high-strength (hot rolled) conditions has been included in NACE Standard MR01-75/ ISO 15156-3 “Sulfide Stress Cracking Resistant Metallic Material for Oil Field Equipment,” at hardness levels up to HRc 35 maximum. | |
Corrosion properties | Field service experience have shown that NITRONIC® 50 stainless has excellent resistance to sulfide stress cracking in air conditions. | |
Heat Treatment | Annealed, for most applications, the 1066°C condition should be selected, as it provides a higher level of mechanical properties along with excellent corrosion resistance. A high strength version can also be supplied with min. yield at 585MPa. |