General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 3.8 % Show Supplier Material materials with Absorción de agua of 3.8 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.6 g/cm³ Show Supplier Material materials with Densidad of 1.6 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 0.9 % Show Supplier Material materials with Moisture absorption of 0.9 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 2.4 % Show Supplier Material materials with Elongación of 2.4 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 15.7 GPa Show Supplier Material materials with Módulo de flexión of 15.7 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 17.7 GPa Show Supplier Material materials with Módulo elástico of 17.7 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 360 MPa Show Supplier Material materials with Resistencia a la flexión of 360 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 250 MPa Show Supplier Material materials with Resistencia a la tracción of 250 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | -30 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | dry | ISO 179/1eA | |
23 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | dry | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 75 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 75 kJ/m² | dry | ISO 179/1eU | -30°C | |
90 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | dry | ISO 179/1eU | 23°C |
Aplicaciones térmicas
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 650 °C Show Supplier Material materials with Glow Wire Flammability Index of 650 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Temperatura de flexión bajo carga | 245 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 245 °C | ISO 75/2Af | 1.80 MPa | ||||
Temperatura de fusión | 258 °C Show Supplier Material materials with Temperatura de fusión of 258 °C | ISO 11357-1/-3 | 10°C/min | ||||
Inflamabilidad | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Eléctrico
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | 290/120/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.4 % Show Supplier Material materials with Contracción of 0.4 % | 290/120/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Light stabilized or stable to light, UV Stabilized, Heat Stabilized | |
| Fillers | 50% Glass Fiber | |
| Processing methods | Injection Molding | |