Propiedades
General
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Densidad | 1.39 g/cm³ Show Supplier Material materials with Densidad of 1.39 g/cm³ | dry | ISO 1183 |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 3.3 % Show Supplier Material materials with Elongación of 3.3 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 10.4 GPa Show Supplier Material materials with Módulo de flexión of 10.4 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 10.8 GPa Show Supplier Material materials with Módulo elástico of 10.8 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 315 MPa Show Supplier Material materials with Resistencia a la flexión of 315 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 209 MPa Show Supplier Material materials with Resistencia a la tracción of 209 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | dry | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 86 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 86 kJ/m² | dry | ISO 179/1eU | 23°C | |
Resistencia al choque, ensayo Izod entallado | 23 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 14 kJ/m² | dry | ISO 180/1A |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de fusión | 262 °C Show Supplier Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <100 ,method: ISO 3795 and thickness tested (mm): 2 | ||||
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Fillers | 33% Glass Fiber | |
| Processing methods | Injection Molding | |