Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 3.15 g/cm³ Show Supplier Material materials with Densidad of 3.15 g/cm³ | For ceramic structural parts |
Tamaño de los cristales | 43169 μm Show Supplier Material materials with Tamaño de los cristales of 43169 μm |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.21 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.21 [-] | For ceramic structural parts |
Módulo elástico | 23.0 °C | 410 GPa Show Supplier Material materials with Módulo elástico of 410 GPa | For ceramic structural parts |
Plane-Strain Fracture Toughnes | 23.0 °C | 4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 4 MPa·√m | For ceramic structural parts |
Resistencia a la compresión | 23.0 °C | 3500 MPa Show Supplier Material materials with Resistencia a la compresión of 3500 MPa | For ceramic structural parts |
Resistencia a la flexión | 23.0 °C | 480 MPa Show Supplier Material materials with Resistencia a la flexión of 480 MPa | For ceramic structural parts |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 23.0 °C | 880 J/(kg·K) Show Supplier Material materials with Calor específico of 880 J/(kg·K) | For ceramic structural parts |
Coeficiente de dilatación térmica | 23.0 °C | 4.4E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4.4E-6 1/K | For ceramic structural parts |
Conductividad térmica | 23.0 °C | 150 W/(m·K) Show Supplier Material materials with Conductividad térmica of 150 W/(m·K) | For ceramic structural parts |
Temperatura máx. de funcionamiento | 1600 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 1600 °C | For ceramic structural parts |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Used in semiconductor and coating industries, As a bearing material for magnetic drive pumps for many years. It is useful in a variety of applications including spray nozzles, shot blast nozzles and cyclone components | |
| Chemical composition | SiC, ZrO2, Si3N4 | |
| Processing history | Sintered | |