General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.2 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.2 [-] | For ceramic structural parts |
Módulo elástico | 23.0 °C | 393 GPa Show Supplier Material materials with Módulo elástico of 393 GPa | For ceramic structural parts |
Plane-Strain Fracture Toughnes | 23.0 °C | 4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 4 MPa·√m | For ceramic structural parts |
Resistencia a la flexión | 23.0 °C | 462 MPa Show Supplier Material materials with Resistencia a la flexión of 462 MPa | For ceramic structural parts |
Resistencia a la tracción | 23.0 °C | 307 MPa Show Supplier Material materials with Resistencia a la tracción of 307 MPa | For ceramic structural parts |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 880 J/(kg·K) Show Supplier Material materials with Calor específico of 880 J/(kg·K) | For ceramic structural parts |
Coeficiente de dilatación térmica | 23.0 °C | 4.3E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4.3E-6 1/K | For ceramic structural parts |
Conductividad térmica | 23.0 °C | 125 W/(m·K) Show Supplier Material materials with Conductividad térmica of 125 W/(m·K) | For ceramic structural parts |
Temperatura máx. de funcionamiento | 1000 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 1000 °C | For ceramic structural parts |
Technological properties
Property | ||
---|---|---|
Application areas | Used in semiconductor and coating industries, As a bearing material for magnetic drive pumps for many years. It is useful in a variety of applications including spray nozzles, shot blast nozzles and cyclone components | |
Chemical composition | SiC, ZrO2, Si3N4 | |
Processing history | Reaction Bonded |