Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | -40.0 °C | 50 J Show Supplier Material materials with Charpy impact energy, V-notch of 50 J | |
Elongación | 23.0 °C | 30 % Show Supplier Material materials with Elongación of 30 % | |
Límite elástico Rp 0,2 | 23.0 °C | 530 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 530 MPa | T<10MM |
Resistencia a la tracción | 23.0 °C | 700 MPa Show Supplier Material materials with Resistencia a la tracción of 700 MPa |
Chemical properties
Property | Value |
---|---|
Azufre | 0.015 % Show Supplier Material materials with Azufre of 0.015 % |
Carbono | 0.04 % Show Supplier Material materials with Carbono of 0.04 % |
Cobre | 0.1 - 0.8 % Show Supplier Material materials with Cobre of 0.1 - 0.8 % |
Cromo | 21 - 22 % Show Supplier Material materials with Cromo of 21 - 22 % |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % |
Hierro | Balance |
Manganeso | 4 - 6 % Show Supplier Material materials with Manganeso of 4 - 6 % |
Molibdeno | 0.1 - 0.8 % Show Supplier Material materials with Molibdeno of 0.1 - 0.8 % |
Nitrógeno | 0.2 - 0.25 % Show Supplier Material materials with Nitrógeno of 0.2 - 0.25 % |
Níquel | 1.35 - 1.9 % Show Supplier Material materials with Níquel of 1.35 - 1.9 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Technological properties
Property | ||
---|---|---|
Application areas | Ideal for tank production where corrosion strength is sufficient | |
Corrosion properties | High resistance to stress corrosion cracking, Good resistance to general corrosion.PREN=26 | |
Heat Treatment | Solution annealing at 1020 – 1100°C followed by water quenching. | |
Welding | Very good |