Medidas
Property | Value |
---|---|
Diámetro | 12.7 - 406.4 mm Show Supplier Material materials with Diámetro of 12.7 - 406.4 mm |
Mecánica
Property | Temperature | Value |
---|---|---|
Charpy impact energy, V-notch | -46.0 °C | 45 J Show Supplier Material materials with Charpy impact energy, V-notch of 45 J |
Dureza Brinell | 23.0 °C | 310 [-] Show Supplier Material materials with Dureza Brinell of 310 [-] |
Elongación | 23.0 °C | 25 % Show Supplier Material materials with Elongación of 25 % |
Límite elástico Rp 0,2 | 23.0 °C | 550 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 550 MPa |
Resistencia a la tracción | 23.0 °C | 750 MPa Show Supplier Material materials with Resistencia a la tracción of 750 MPa |
Chemical properties
Property | Value |
---|---|
Azufre | 0.01 % Show Supplier Material materials with Azufre of 0.01 % |
Carbono | 0.03 % Show Supplier Material materials with Carbono of 0.03 % |
Cobre | 0.5 - 1 % Show Supplier Material materials with Cobre of 0.5 - 1 % |
Cromo | 24 - 26 % Show Supplier Material materials with Cromo of 24 - 26 % |
Fósforo | 0.03 % Show Supplier Material materials with Fósforo of 0.03 % |
Hierro | Balance |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % |
Molibdeno | 3 - 4 % Show Supplier Material materials with Molibdeno of 3 - 4 % |
Nitrógeno | 0.2 - 0.3 % Show Supplier Material materials with Nitrógeno of 0.2 - 0.3 % |
Níquel | 6 - 8 % Show Supplier Material materials with Níquel of 6 - 8 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Wolframio | 0.5 - 1 % Show Supplier Material materials with Wolframio of 0.5 - 1 % |
Technological properties
Property | ||
---|---|---|
Application areas | It is widely used in oil & gas, hydropower, pressure vessels, pulp & paper, structural components and chemical tankers. | |
Corrosion properties | High resistance to stress corrosion cracking in halide containing environments, High resistance to pitting and crevice corrosion, High resistance to general corrosion, High resistance to erosion corrosion and corrosion fatigue. PREN ≥ 40 | |
Heat Treatment | Solution annealing at 1100°C followed by water quenching. | |
Welding | Very good |